Polymer Innovation Blog

Practical tips and advice for polymer, innovation and product development professionals

Polymer Innovation
  • Home
  • eBooks
    • Polymers in Electronic Packaging
    • Rheology of Thermosets eBook
    • Practical Tips for Curing Thermosets
    • Thermoset Characterization
    • Dielectric Cure Monitoring of Thermosets
    • Introduction to Biopolymers and Bioplastics
  • Videos
    • Core Curriculum: 3 Part Video Series
    • Characterization of Thermosets: 4 Part Video Series
    • Advanced Thermoset Cure Kinetics: 3 Part Video Series
    • DSC of Polymers: 5 Part Video Series
    • Thermoplastics: 5 Part Video Series
  • Services
    • Consulting
    • Polymer Expert Witness
  • Learning Center
    • White Paper
  • Why Jeff?
    • Speaker Info
  • Contact
  • Subscribe
  • Members
    • Login
    • Logout

Thermoset Characterization Part 12: Introduction to Thermogravimetric Analysis (TGA)

June 30, 2014 By Jeffrey Gotro Leave a Comment

Guest Post by Dr. R. Bruce Prime

Thermogravimetric analysis or TGA is a technique where the mass (or weight) of a material is measured as a function of temperature or time while the sample is subjected to a controlled temperature program in a controlled atmosphere [Earnest, ASTM STP 997 (1988)].

TGA Balance

Temperature ranges for commercial TGAs are typically ambient to 1000°C or higher, more than sufficient for thermoset applications. As shown in the illustration a purge gas flowing through the balance creates an atmosphere that can be inert such as nitrogen or oxidizing such as air or oxygen. Additionally, the moisture content of the purge gas can be controlled anywhere between dry and saturated. Typical sample size ranges from less than a milligram to a gram or more.

Thermosets generally exhibit mass loss, which falls into three categories: volatile components, reaction products, and decomposition products. All of these mass loss processes may be characterized by TGA to yield information such as moisture content, residual solvent, composition, extent of cure and thermal stability. The kinetics of these processes may also be determined to model and predict cure and aging due to thermal and thermooxidative processes. Kinetics will be the subject of future posts.

TGA and DTGA

The TGA plots above show the degradation of a polymer when heated at 10°C/min and illustrate several attributes of TGA. The polymer is poly(vinyl methyl ether) or PVME, a key component of a thermosetting disk coating [Prime et al., Soc. Plast. Eng. Proc. Ann. Conf. 34, 1268 (1988)]. Notice that the degradation in nitrogen is simple with one major mass loss step that begins above 300°C, whereas in air three mass loss processes are observed with the first beginning around 200°C. Advantages of the derivative d(mass)/dt or DTG curves are also evident. The three mass loss processes in an oxidizing environment are much easier to distinguish. And the enhanced sensitivity of the DTG curve is illustrated in the 25°C earlier detection of the onset of degradation in air than is observed in the TGA curve.

TGA Phenolic Cure

This set of TGA curves for a phenolic resin illustrates the application of TGA to the measurement of cure for thermosets whose cure chemistry involves a distinct mass loss (e.g. water or formaldehyde) for each bond that is formed. The uncured resin shows a very small mass loss due to absorbed water that is only observed in the DTG curve plus a two-stage cure process with a total mass loss of 3%. Data on the two partially cured samples offer valuable insight into the cure process plus an estimate of the degree of cure. Note that cure of this material could not be measured by DSC because the cure exotherm would be altered or masked by the endothermic evaporation of the reaction products.

TGA Composition

The example above clearly shows the composition of a silver-filled thermosetting ink from the two distinct mass loss steps. This is typical of an ink used in screen-printing. TGA was run at 5°C/min in air.

To summarize, TGA of thermosets yields valuable information on:

  • Volatile components: absorbed moisture, residual solvents, additives/oligomers from ambient to 200°C
  • Reaction products, e.g. from cure of phenolic resins, blocked catalysts from 100 to 250°C
  • Volatile degradation products from 250 to 800°C

In the next post we will explore more applications of TGA to thermosets.

Share on LinkedIn Share

Filed Under: Uncategorized

« Thermoset Characterization Part 11: Applications of Thermomechanical Analysis (TMA)
Happy Fourth of July »

Leave a Reply

Your email address will not be published. Required fields are marked *

Polymer Innovation Blog

I’m Dr. Jeff Gotro and welcome to the Polymer Innovation Blog. Over the last 40 years I have been involved in polymer research, along with product and process development. I acquired invaluable experience working for IBM, AlliedSignal, Honeywell, Ablestik Labs (now Henkel) and in multiple consulting projects. In this blog, I (along with some guest contributors) will share our experiences, tips, and “tricks of the trade” to get more out of your innovation efforts and discuss new trends and technical advances in the polymer industry.
View Jeff Gotro, Ph.D., CMC's profile on LinkedIn

Innocentrix, LLC


Click to Visit Website

plastics expert witness
Click for More Information

Subscribe by Email

Search the Blog

Polymer Video Training

Visit our Video Store

Polymers in Electronic Packaging

polymers in electronic packaging Are you confused about what is electronic packaging? Have you ever wondered what type of polymers and polymer-based composites are used in electronics? Learn More...

Practical Tips for Curing Thermosets

practical tips for curing thermosets Have you ever had a question about the degree of cure or is your part fully cured after processing? Confused about what is gelation or how does vitrification impact thermoset curing? Learn More...

Rheology of Thermosets

rheology of thermosets Have you ever had a question about measuring the rheological properties of thermosets Didn’t know what is the right experimental approach to get the right rheological information? Learn More...

Dielectric Cure Monitoring of Thermosets

Dielectric Cure Monitoring of Thermosets Do you have a need for an in-situ cure monitor for a thermoset process but don’t know where to start? Are you confused about the terminology used in dielectric spectroscopy? Learn More...

Introduction to Biopolymers and Bioplastics

Introduction to Biopolymers and Bioplastics Would you like to know how sustainable are bio-based polymers? Or what is the market size and growth rate for bioplastics? Or have questions about the biomass supply chain? Learn More...

Thermoset Characterization

Thermoset Characterization Have you ever had a question about how to measure a physical property of a thermoset? Confused about what is gelation or how does vitrification impact thermoset curing profiles? Or wondered how to measure the glass transition temperature of an epoxy or polyester composite? Learn More...

Amazon.com Bookshelf

Robert's Rules of Innovation Thermal Analysis of Polymers Order

Copyright © 2025 Innocentrix, LLC · All Rights Reserved